Showing 21-29 of 29 items.
Mixes
User | Date | Mix ID | Type1 | Type2 | Actions | ||
---|---|---|---|---|---|---|---|
MaterialsMaterial
Weight g (%)
Material Family
Commercial Name
Price
True Density
Bulk Density (g/cc)
Koranel_GB
25.6 (25.60 %)
Industrial Slag / Glass
Sand
62.8 (62.80 %)
Coarse Aggregate
SiO2/Na2O molar ratio 1.6 and 70 wt% H2O
11.6 (11.60 %)
Alkali-silicate
Placing & CuringShaping
De-Airing
Curing conditions
Duration (Mins)
Conditions after curing
Duration (Mins)
Casting
Jolting
20-22°C & 60-70% Humidity
Wrapped
0 | Pooya | 2023-02-10 12:24:45 | 48 | Inorganic Polymer | Alkali-activated | ||
MaterialsMaterial
Weight g (%)
Material Family
Commercial Name
Price
True Density
Bulk Density (g/cc)
Koranel_GB
140.89 (39.37 %)
Industrial Slag / Glass
Modified basic-oxygen-furnace slag
25.75 (7.20 %)
Industrial Slag / Glass
M2
50.79 (14.19 %)
Laboratory Slag / Glass
C1 sag
140.43 (39.24 %)
Laboratory Slag / Glass
Placing & CuringShaping
De-Airing
Curing conditions
Duration (Mins)
Conditions after curing
Duration (Mins)
24 | Afsar | 2023-03-06 13:11:53 | 55 | Inorganic Polymer | - | ||
MaterialsMaterial
Weight g (%)
Material Family
Commercial Name
Price
True Density
Bulk Density (g/cc)
M2
100 (100.00 %)
Laboratory Slag / Glass
Placing & CuringShaping
De-Airing
Curing conditions
Duration (Mins)
Conditions after curing
Duration (Mins)
Casting
Vibration
20-22°C & 60-70% Humidity
Wrapped
Hardened PropertiesStandard (Mortar)
Standard (Concrete)
Value
Standard Deviation
17.1
-
-
-
27.1
-
-
-
DurabilityStandard (Mortar)
Standard (Concrete)
Value
Standard Deviation
-
-
0.12
-
-
-
20.4
-
| nana.wen@student.kuleuven.be | 2023-04-07 12:48:36 | 84 | Inorganic Polymer | Chemical-Resistant | ||
MaterialsMaterial
Weight g (%)
Material Family
Commercial Name
Price
True Density
Bulk Density (g/cc)
Vitrified red mud - 1st pilot trial
550 (25.29 %)
Industrial Slag / Glass
Sodium silicate solution SiO/Na2O = 2.0, 65% H2O
275 (12.64 %)
Alkali-silicate
Sand
1350 (62.07 %)
Coarse Aggregate
Placing & CuringShaping
De-Airing
Curing conditions
Duration (Mins)
Conditions after curing
Duration (Mins)
Casting
Tapping
20-22°C & 60-70% Humidity
1
Wrapped
Fresh PropertiesStandard (Mortar)
Standard (Concrete)
Value
Standard Deviation
217
-
-
-
Hardened PropertiesStandard (Mortar)
Standard (Concrete)
Value
Standard Deviation
-
-
38.9
6.1
-
-
78.7427
3.71781
-
-
93.9797
2.71494
| Giels | 2023-04-12 15:39:07 | 86 | Inorganic Polymer | Others | ||
| rr22 | 2023-02-10 12:32:50 | 50 | Cement | Rapid-Hardening | ||
| fabiocabral | 2023-02-10 12:12:00 | 38 | Alkali-activated | - | ||
MaterialsMaterial
Weight g (%)
Material Family
Commercial Name
Price
True Density
Bulk Density (g/cc)
Bauxite residue
25 (25.09 %)
Tailing
Cement 52.5N
24.35 (24.44 %)
Portland Cement
Sand
50 (50.18 %)
Coarse Aggregate
Gypsum
0.3 (0.30 %)
Mineral
| Kosar | 2023-02-10 12:13:56 | 40 | Alkali-activated | Porous | ||
| fabiocabral | 2023-02-10 12:14:32 | 41 | Alkali-activated | - | ||
MaterialsMaterial
Weight g (%)
Material Family
Commercial Name
Price
True Density
Bulk Density (g/cc)
Koranel_GB
34.7 (34.71 %)
Industrial Slag / Glass
Sand
52.08 (52.10 %)
Coarse Aggregate
SiO2/Na2O molar ratio 1.6 and 70 wt% H2O
13.19 (13.19 %)
Alkali-silicate
Placing & CuringShaping
De-Airing
Curing conditions
Duration (Mins)
Conditions after curing
Duration (Mins)
Casting
Jolting
20-22°C & 60-70% Humidity
1
Wrapped
0 | Glenn | 2023-02-10 12:21:00 | 45 | Alkali-activated | Self-Levelling | ||